The metal and its alloys

Tinplate

A major end use for tin is tinplate, which accounts for about 30 percent of total tin consumption. Tinplate is basically a steel product with a tin coating that may be only one micrometre (0.00004 inch) thick.

Until the middle of the 20th century, tinplate was manufactured in specially designed tinning plants by immersing individual sheets in a bath of molten tin. This hot-dip method has been superseded by a continuous electroplating process, in which tin is plated directly onto a moving steel strip. A typical modern electrolytic tinplate line operates at speeds up to 600 metres (2,000 feet) per minute and has an annual productive capacity of some 300,000 tons, with a consumption of about 1,800 tons of tin.

Approximately 90 percent of all tinplate finds its way into the packaging industry, with the remainder going into light engineering uses. Tinplate cans are used for virtually all kinds of processed foods and for a host of other products.

The traditional tinplate can is built up from three pieces of metal: a cylindrical body, formed from a rectangular blank and with a locked and soldered side seam; and two ends, one seamed on by the can maker and the other by the packer after the can is filled. This type of can has been virtually replaced by one with a welded side seam. In addition, a new type of two-piece tinplate container, this one with a drawn and wall-ironed seamless body, was developed initially for the beer and soft-drinks market but has extended into food packaging.

Although tinplate is a traditional product, it is a continually evolving one. As an example, in 1965 the average thickness of a can wall was about 0.25 millimetre (0.01 inch). In 1990 it was about 0.18 millimetre or, in the two-piece can, as little as 0.10 to 0.15 millimetre.

Tin and tin-alloy coatings

The properties of tin make it ideal for use as a coating. Owing to the low melting point of tin, and because it readily alloys with most other metals, tin coatings can easily be produced by immersing a suitably prepared metal object in a bath of molten tin. Hot-dipped tin coatings present a good appearance and are tightly adherent. When coated sheets are severely drawn and worked, the coating, rather than flaking off, acts beneficially as a lubricant.

Tin coatings may also be produced by electroplating the metal from an aqueous solution of its salts. Both bright and matte-finish tin coatings can be produced.

The value of tin as a coating metal is further enhanced by a wide range of tin-alloy coatings, each with its own specific properties and applications. Among the commercial electroplated coatings in common use are tin-zinc, tin-nickel, tin-copper, and tin-lead. These are used as both protective and decorative finishes. Tin-zinc coatings are used for a number of industrial applications, especially in the automotive industry. Tin-nickel is highly resistant to corrosion and tarnish, finding special use in electrical equipment and scientific instruments. The appearance of tin-copper coatings ranges from a bronze colour to white, depending on the proportions of copper and tin. Tin-lead alloys can be applied by electroplating and by hot-dipping; they are extensively used to provide solderable surfaces on other metals. Tin-lead coatings on steel sheet (known as terneplate) are used for long-term outdoor corrosion protection and also for gasoline tanks.

Tin-based solders

A second large application of tin is in solders for joining metals. The most common solders are basically alloys of lead and tin. Since these metals can be alloyed across the whole range of proportions, an infinite number of compositions is possible; in practice, though, most solders contain from 30 to 70 percent tin, with occasional minor additions for special purposes. Apart from one alloy—the eutectic 62-percent-tin–38-percent-lead alloy, which melts at 183 °C (361 °F)—all tin-lead solders soften over a temperature range before melting; this “pasty range” is made use of in certain molding and wipe-soldering applications.

The major application of solders is for making electrical connections in the electrical and electronics industries. Much modern equipment, particularly in electronics, is now assembled on high-speed, automated production lines in which large numbers of soldered connections are made simultaneously. A further development in electronics is surface-mounted technology, in which the components (often very complicated microcircuits) are not attached by wire leads but are soldered directly onto the circuit boards.

Special tin-based solders have been developed for specific applications. For example, lead-free solders are produced for use in domestic water systems, especially for drinking water. These are essentially high-tin alloys with a few percent copper or silver added.

Low-temperature casting alloys

Apart from joining metals, solders are also used as low-melting-point casting alloys. Allied to solders in this application are the so-called fusible alloys. Usually more complex alloy systems than the simple solders, fusible alloys may contain bismuth, cadmium, antimony, and occasionally indium and gallium.

In addition to their low melting points, fusible alloys have other distinctive properties. For example, by careful selection of the constituent metals, alloys can be obtained that either grow on solidification, remain dimensionally stable, or shrink to predetermined degrees. Fusible alloys that expand on solidification are used in machining to embed small, complex objects that must be held fast. Other alloys are used in pipe bending and forming as temporary internal mandrels or supports that can be melted out at low temperature after use.

Fusible alloy systems that melt at price temperatures also can be produced. These are used as safety thermal fuses—e.g., in fire detection or fire control apparatuses—or as temperature indicators in components such as test bearings, where other forms of temperature indication cannot be employed. Other fusible alloys are used as sealing materials for special applications, such as double-glazing panels.

Bronze

The alloying of copper and tin to form bronze predates written history, and yet bronze continues to be an important industrial use for tin. Tin bronzes are alloys of tin with copper, copper-lead, and copper-lead-zinc. Cast bronzes contain up to 12 percent tin—except for special applications such as bells and musical instruments, in which a tin content up to 20 percent imparts required tonal qualities. Leaded bronzes, containing up to 15 percent lead, are used in heavy-duty bearings. The zinc-containing alloys, known as gunmetals, are cheaper than tin bronzes and are used in valves and fittings for steam and water lines.

Bearing alloys

Alloys of tin with about 7 percent antimony and 3 percent copper have proved to be the best materials for plain bearings running against a steel shaft. Known as tin-based babbitt metals or white metals, they owe their reputation to the ability to deform sufficiently in order to compensate for irregularities in the bearing assembly, to embed foreign particles in order to prevent scoring, and to retain oil films on their surfaces. White-metal bearings are cast onto steel, bronze, or cast-iron backing shells. However, in applications where bearings are highly loaded, the strength of tin-rich alloys may be insufficient, so that an alloy of 80 percent aluminum and 20 percent tin is customarily used. This alloy, bonded to a steel or bronze shell, is widely used in diesel engines and in the high-performance engine of most automobiles.